Jam Petrochemical 22501AA LLDPE Datasheet
22501 is a LLDPE blown film grade designed for applications requiring good optical properties even at low extrusion temperature. This resin combines ease of processing with low gels and it is well suited for blending with LDPE and for general purpose applications.
General Properties
Grade Name
22501AA
Manufacturer
Jam Petrochemical
Datasheet
Download
Categories
Polymer, Thermoplastic, Polyethylene, Linear Low Density Polyethylene
Processing Methods
Blown Film
Applications
Film, Light-Duty Films
Features
Low Gel Level, Good Optical Properties, Good Stiffness, Good Processability
Physical Properties
Value
Unit
Test Conditions
Test Method
Density
0.922
g/cm³
ASTM D1505
MFI
0.95
g/10min
ASTM D1238
Mechanical Properties
Value
Unit
Test Conditions
Test Method
Film Elongation at Break, MD
680
%
ASTM D882
Film Elongation at Break, TD
780
%
ASTM D882
Film Tensile Modulus, MD
200
MPa
2%Secant Modulus
ASTM D882
Film Tensile Modulus, TD
240
MPa
2%Secant Modulus
ASTM D882
Film Tensile Strength at Break, MD
45
MPa
ASTM D882
Film Tensile Strength at Break, TD
30
MPa
ASTM D882
Film Tensile Strength at Yield, MD
13
MPa
ASTM D882
Film Tensile Strength at Yield, TD
12.5
MPa
ASTM D882
Impact Strength, Dart
80
gr
ASTM D1709
Tear Propagation Resistance, MD
105
gram-force
Elmendorf method
ASTM D1922
Tear Propagation Resistance, TD
460
gram-force
Elmendorf method
ASTM D1922
Optical Properties
Value
Unit
Test Conditions
Test Method
Gloss
38
45°
ASTM D2457
Haze
21
%
ASTM D1003
Disclaimer
The information presented on this datasheet was acquired by Tecves from the producer of the material. Tecves makes substantial efforts to assure the accuracy of this data. However, Tecves assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.
Share
Share on Facebook
Share on Twitter
Share on Linkedin
Share on Telegram
Contact Form
Request a new material, suggest an improvement or report a bug in datasheet.