Regal Petrochemical RG 1101XXR PP Homo Datasheet

Homopolymer with antigasfading stabilization and inherent UV stability

General Properties

Grade Name
RG 1101XXR
Regal Petrochemical
Polymer, Thermoplastic, Polypropylene, Polypropylene Homopolymer
Processing Methods
Extrusion, Fiber Forming
Carpets and Rugs, Laminate Film, Partially Oriented Yarn, Continuous Filament, Drawn Textured Yarn, Bulk Continuous Filament
Good UV Resistrance, Gas Fading Stabilized

Physical Properties

Value Unit Test Conditions Test Method
Density 0.91 g/cm³ ASTM D792
MFI 23 g/10min At 21.6Kg, 230°C ASTM D1238

Mechanical Properties

Value Unit Test Conditions Test Method
Charpy Impact Notched 2.5 kJ/m² At 23°C ISO 179/1eA
Charpy Impact Notched 1.5 kJ/m² At -30°C ISO 179/1eA
Hardness Ball Indentation 78 MPa ISO 2039-1
Tensile Elongation at Yield 8 % 50mm/min ASTM D638
Tensile Modulus 1500 MPa 1mm/min ASTM D638
Tensile Strength at Yield 35 MPa 50mm/min ASTM D638

Thermal Properties

Value Unit Test Conditions Test Method
Heat Deflection Temperature 85 At 0.46MPa ASTM D648
Melting Point 163 DSC Analysis ASTM D3417
Vicat Softening Point 154 10N ASTM D1525


The information presented on this datasheet was acquired by Tecves from the producer of the material. Tecves makes substantial efforts to assure the accuracy of this data. However, Tecves assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.