Regal Petrochemical RG 1102M PP Homo Datasheet
Homopolymer for extrusion and thermoforming applications with good processing stability
General Properties
Grade Name
RG 1102M
Manufacturer
Regal Petrochemical
Datasheet
Download
Categories
Polymer, Thermoplastic, Polypropylene, Polypropylene Homopolymer
Processing Methods
Extrusion, Injection Molding, Blown Film, Thermoforming, Cast Film, Fiber Forming
Applications
Film, BOPP Film, Thermoforming Sheet, Yarn, Raffia
Features
Good Processability
Physical Properties
Value
Unit
Test Conditions
Test Method
Density
0.91
g/cm³
ASTM D792
MFI
8
g/10min
At 21.6Kg, 230°C
ASTM D1238
Mechanical Properties
Value
Unit
Test Conditions
Test Method
Charpy Impact Notched
3.5
kJ/m²
At 23°C
ISO 179/1eA
Charpy Impact Notched
1.6
kJ/m²
At -30°C
ISO 179/1eA
Hardness Ball Indentation
77
MPa
ISO 2039-1
Tensile Elongation at Yield
9
%
50mm/min
ASTM D638
Tensile Modulus
1500
MPa
1mm/min
ASTM D638
Tensile Strength at Yield
35
MPa
50mm/min
ASTM D638
Thermal Properties
Value
Unit
Test Conditions
Test Method
Heat Deflection Temperature
85
C°
At 0.46MPa
ASTM D648
Melting Point
163
C°
DSC Analysis
ASTM D3417
Vicat Softening Point
154
C°
10N
ASTM D1525
Disclaimer
The information presented on this datasheet was acquired by Tecves from the producer of the material. Tecves makes substantial efforts to assure the accuracy of this data. However, Tecves assumes no responsibility for the data values and strongly encourages that upon final material selection, data points are validated with the material supplier.
Share
Share on Facebook
Share on Twitter
Share on Linkedin
Share on Telegram
Contact Form
Request a new material, suggest an improvement or report a bug in datasheet.